ACLAR^® Fluoropolymer Film

The "miracle film" for tissue culture and epoxy embedding applications!

A few not-generally-known words about ACLAR Fluoropolymer Films
There is an entire family of ACLAR Fluoropolymer Films and the different ACLAR "grades" or products, represent different chemistries. The ACLAR film found to be the most ideal for applications in microscopy and histology is ACLAR 33C and it has traditionally been used in 5 mil thickness. This is a polychlorotrifluoroethylene copolymer and this particular composition results in a film with very excellent optical properties, as well as good thermal and chemical stability. It also serves as an excellent moisture barrier. It is always recommended that the user take advantage of a wide range of other information that is known about ACLAR 33C. The high UV transparency of this particular grade of ACLAR makes it idea for use in the UV curing of resins in microscopy and histology.

However, the manufacturer of ACLAR films has discontinued the production of the 5 mil film and only offers the film in 2 and 7.8 mils. For a while, we believed that 2 mils is just not thick enough for applications in microscopy, and we started offering 7.8 mil thickness. But now we have found that some users actually show a preference for the 2 mil thick product. Apparently, the more pliable nature of the thinner product makes it easier to get a good barrier seal against oxygen.

Conclusion: If you have been using the 5 mil ACLAR product, and if you were to use the 7.8 mil product, you would see virtually no difference, except for the slightly higher stiffness of the thicker film. The optical properties and UV transparency is essentially the same. But if you were to try the thinner product, in addition to finding it easier to seal, you will be happily surprised to find out that the thinner version of the product is also much less expensive!

We can summarize some of the most desirable qualities of the ACLAR films, all of which are as true of the 2.0 and 7.8 mil products as was for the 5 mil product:

Unsurpassed as a clear, flexible moisture barrier
Crystal clear in optical properties
Chemically stable and biochemically inert
Plasticizer and stabilizer free
Transparent to UV irradiation
No autofluorescence
Nonflammable
Low surface energy and non-aging
Low dielectric constant and dissipation factor; high dielectric strength
Stable under the electron beam of an SEM

Some comments specific to use in microscopy and histology laboratories
The fluorinated-chlorinated polymers, because of the fluorinated aspect of the system, exhibit, in some respects almost PTFE-like properties, and therefore separates easily from all of the commonly used epoxy embedding formulations used in microscopy and histology. It can be applied to glass, such as a glass slide, without there being any real evidence for the presence of the film. Cells adhere quite tenaciously to the ACLAR surface, despite the PTFE nature, and they will stay attached through all of the commonly used processing methods such as fixation and dehydration, embedding and even critical point drying. Although the 5 mil film sectioned quite acceptably, we are told that the 2 mil product sections even easier. That is why it is often times called an "embedding" film, which is why we call the 2 mil product "new and improved".

The film, with attached cells, after critical point drying, can be conventionally sputter coated with gold or other precious metals and for high resolution work in a FESEM, it can be osmium coated or chromium coated. For critical point drying, since the 7.8 mil film is more robust and won't flop around as readily as the 2 mil product, we recommend the thicker film. But good results are indeed possible with the 2 mil product as well.

And finally, the film shows no signs of deterioration even after long term exposure to UV.

ACLAR 33C film can be cut with a fairly ordinary scissors and reportedly, does not damage diamond knives during sectioning.

Resistance to osmium tetroxide:
The ACLAR films do not have the intertness of PTFE, but they are have enough fluorinated character to exhibit far more chemical resistance than a non-fluorinated polyolefin.

One word of caution:
Because of the Cl content in the film, we would urge caution before using ACLAR film in conjunction with any EDS work because of the large count rate that would be coming from the presence of Cl in the film. In general, we would recommend against use of this film when EDS is contemplated, unless of course there were no other alternatives which often times could be the case.

ACLAR 33C Film Dimensions
Thickness: 2.0 mils (0.0020"/50.8 ľm)
Lateral Dimensions: 8x10" (203 x 254 mm)
Thickness: 7.8 mils (0.0078"/198 ľm)
Lateral Dimensions: 12.5x8" (317 x 203 mm)

Custom dimensions: Tell us your requirements, we can cut to any size provided minimum quantities are ordered. Maximum dimension is 12.5", however, if orders are large enough, we can offer custom cut film up to 18" on a side. When considering prices, note that the 7.8 mil thick Aclar is a larger size sheet than is the 2.0 mil sheet or Aclar sheets obtained from other sources.

	SPI #	Each	In Stock
ACLAR 33C Film Thickness: 2.0 mils (0.0020"/50.8 ľm) Lateral Dimensions: 8x10" (203 x 254 mm)
Pack of 25 sheets	01859-CF	$77.66	Yes
Pack of 100 sheets	01859-MB	225.00	No

Thickness: 7.8 mils (0.0078"/198 ľm) Lateral Dimensions: 12.5x8" (317 x 203 mm) Note larger size!
Pack of 25 sheets	01858-CF	$181.19	Yes
Pack of 100 sheets	01858-MB	400.00	Yes

Storage conditions: Room temperature
Non-hazardous from stand point of shipping

To Ask a Question or Make a Comment

To Place an Order or Request a Quote

Return to:

Tuesday May 13, 2008 © Copyright 2000 - 2008. By Structure Probe, Inc.
Contacting SPI Supplies and Structure Probe, Inc.
All rights reserved.
All trademarks and trade names are the property of their respective owners.
Privacy Policy

Worldwide Distributors, Representatives, and Agents Flag logo

ACLAR® Fluoropolymer Film

ACLAR^® Fluoropolymer Film